Method for dicing a semiconductor wafer

ABSTRACT

A method for dicing a semiconductor wafer to dice which comprises: 
     (a) placing and fixing the wafer on a dicing film which comprises a base film permeable to ultraviolet light and a layer of a pressure sensitive adhesive formed on one side of the base film to fix thereon the wafer, the adhesive comprising: 
     (i) at least one elastic polymer selected from the group consisting of polyacrylic acid ester copolymers and saturated copolyesters; 
     (ii) an ultraviolet light polymerizable acrylic acid ester having not less than two acryloyl or methacryloyl groups in the molecule and having a molecular weight of not more than about 1000, in amounts of about 15-200 parts by weight in relation to 100 parts by weight of the elastic polymer; and 
     (iii) a photopolymerization initiator in a sufficient amount to induce the photopolymerization of the ultraviolet light polymerizable acrylic acid ester; 
     (b) dicing the wafer; 
     (c) applying the ultraviolet light to the other side of the dicing film to substantially reduce the adhesive force of the dicing film; and then 
     (d) removing the resultant dice from the dicing film.

The present invention relates to a method for dicing a semiconductor wafer to dice wherein the wafer is at first fixed on a pressure sensitive adhesive film for dicing, and after the dicing the adhesive force is reduced by the application thereto of ultraviolet light so that the dice is readily removable from the dicing film.

As is well known, a dicing process is included in the production of integrated circuits. In the process, a semiconductor wafer is placed and fixed on a pressure sensitive adhesive film called a dicing film, cut to small pieces or dices of a predetermined size, and then the dice are removed or picked up from the film. Therefore, it is desirable that the semiconductor wafer, for instance, a silicon wafer, is initially adhered onto the dicing film with a relatively strong adhesive force so as to be precisely diced to dice of a predetermined size, whereas after the dicing the resultant dice is loosely adhered onto the film so as to be readily removable therefrom.

For exemplification only, it is desired that the dicing film initially has an adhesive force of about 100-800 g/25 mm so that the wafer is precisely diced, but after the dicing the film has a reduced adhesive force of several tens grams/25 mm or less for the ready removal of the resultant dice. However, no such a pressure sensitive adhesive which has a substantially reducible adhesive force so as to be suitably and practically usable for dicing a semiconductor wafer has been known to date.

On the other hand, a photocurable adhesive is already known which is curable by the application thereto of ultraviolet light to develop the desired force. The photocurable adhesive is usually composed of a photopolymerizable oligomer, a photopolymerizable monomer, a photopolymerization initiator and other additives, and is rapidly cured by the application thereto of the ultraviolet light. It must be noted, however, that the ultraviolet light is applied to the adhesive to complete the adhesion.

The present inventors have made an intensive investigation of a pressure sensitive adhesive for use in dicing a semiconductor wafer, and found unexpectedly that a photosensitive adhesive mainly composed of a certain elastic polymer as a base resin, a photopolymerizable acrylic acid ester and a photopolymerization initiator is substantially reducible in adhesive force by the application thereto of the ultraviolet light. After a further investigation based on the above finding, the inventors have found that a pressure sensitive adhesive film composed of a photopermeable base film having on one side thereof such a layer of the pressure sensitive adhesive as above mentioned is capable of fixing thereon a semiconductor wafer with a sufficient adhesive force to make it possible for the wafer to be precisely diced, but loses its adhesive force by the irradiation of the ultraviolet light to the other side of the film so that the dice may be readily removed therefrom.

It is, therefore, an object of the invention to provide a method for dicing a semiconductor wafer in which the wafer is initially fixed on a pressure sensitive dicing film so that the wafer is precisely diced to small pieces or dice, and after the dicing, the film is substantially reduced in the adhesive force by the application thereto of the ultraviolet light so that the resultant dice are readily removed therefrom.

The method for dicing a semiconductor wafer according to the invention comprises:

(a) placing and fixing the wafer on a dicing film which comprises a base film permeable to ultraviolet light and a layer of a pressure sensitive adhesive formed on one side of the base film to fix thereon the wafer, the adhesive comprising:

(i) at least one elastic polymer selected from the group consisting of a polymer mainly composed of acrylic acid ester copolymers and a saturated copolyester mainly composed of a dibasic carboxylic acid and a dihydroxy alcohol;

(ii) an ultraviolet light polymerizable acrylic acid ester having not less than two acryloyl or methacryloyl groups in the molecule and having a molecular weight of not more than about 1000, in amounts of about 15-200 parts by weight in relation to 100 parts by weigt of the elastic polymer; and

(iii) a photopolymerization initiator in a sufficient amount to induce the photopolymerization of the ultraviolet light polymerizable acrylic acid ester:

(b) dicing the wafer;

(c) applying the ultraviolet light to the other side of the dicing film to substantially reduce the adhesive force of the dicing film; and

(d) removing the resultant dice from the dicing film.

Other and further objects and features of the invention will be more apparent from the following description.

The dicing film used in the invention is composed of a base film which is permeable to the ultraviolet light and a layer of a pressure sensitive adhesive formed on one side of the base film to fix thereon a semiconductor wafer. The pressure sensitive adhesive includes an elastic polymer as a main component, a photopolymerizable acrylic acid ester polymerizable by the application thereto of the ultraviolet light and a photopolymerization initiator.

A variety of pressure sensitive adhesives are already known, as described, for instance, in "Adhesive Handbook," 2nd ed., edited by Japan Adhesives Association, pp. 398-414 (1980), Nikkan Kogyo Shinbunsha. A typical pressure sensitive adhesive is composed of an elastic polymer as a main component, a tackifier and a plasticizer in which the elastic polymer is soluble, and when desired, additional components such as an antioxidant, a filler and a colorant. According to the invention, however, the pressure sensitive adhesive includes at least one specified polymer as the elastic polymer selected from the group consisting of a polymer mainly composed of acrylic acid esters and a saturated copolyester mainly composed of dibasic carboxylic acids and dihydroxy alcohols.

The acrylic acid ester polymer as the elastic polymer in the pressure sensitive adhesive usable in the invention is already well known in the art, and is normally a copolymer of acrylic acid ester components as main monomer components such as ethyl acrylate, butyl acrylate or 2-ethylhexyl acrylate to form adhesive soft segments of a low glass transition temperature in the polymer chain, and comonomer components such as vinyl acetate, acrylonitrile, styrene, methyl acrylate or methyl methacrylate to form cohesive hard segments of a high glass transition temperature in the polymer chain. The elastic polymer may further include a third comonomer component having a functional group therein such as a carboxyl, a hydroxyl, an amide, a glycidyl or a hydroxyalkyl to improve the curability and/or the adhesion of the resultant polymer. Examples of the third comonomer are acrylic acid, methacrylic acid, itaconic acid, hydroxymethyl methacrylate, hydroxypropyl methacrylate, acryl amide or glycidyl methacrylate.

The saturated copolyester preferably usable as the elastic polymer in the invention is per se also known, as described, for instance, in "Kogyo Zairyo (Industrial Materials)," Vol. 25, No. 11, pp. 101-106 (1977), and is a copolyester composed of a saturated dibasic carboxylic acid component and a saturated dihydroxy alcohol component, i.e., a glycol component. Hence, the copolyester has a low glass transition temperature. A mixture of an aromatic dibasic carboxylic acid and an aliphatic dibasic carboxylic acid is, for example, preferably used as the dibasic carboxylic acid component, while an aliphatic and/or an alicyclic glycol is preferably used as the glycol component.

In the invention, a copolyester is preferred which is composed of a dibasic carboxylic acid component of an aromatic dibasic carboxylic acid and an aliphatic dibasic carboxylic acid in a molar ratio of the former to the latter of about 80/20 to 20/80, more preferably of about 70/30 to 50/50, and a glycol component, substantially in an equimolar ratio. In particular, terephthalic acid is preferred as the aromatic dibasic carboxylic acid, whereas sebacic acid and adipic acid are preferred as the aliphatic dibasic carboxylic acid, meanwhile ethylene glycol, 1,4-butanediol and propylene glycol are, for instance, preferred as the glycol component, for the copolyester suitable for use in the invention. However, the dibasic carboxylic acid component may be in part displaced by a tribasic carboxylic acid, and the glycol may be replaced by a trihydroxy alcohol.

Preferably the pressure sensitive adhesive used in the invention includes a tackfier therein in amounts not more than about 200 parts by weight in relation to 100 parts by weight of the elastic polymer. The tackifier usable in the adhesive in the invention is not restricted to a specified one, but any tackifier is usable which is known in the production of a conventional pressure sensitive adhesive.

As examples only, there are mentioned as such a tackifier, for instance, xylene resins, rosins, polymerized rosins, hydrogenated rosins, rosin esters, terpene resins, terpene-phenol resins, petroleum resins, coumarone resins, styrene resins, alkylphenol resins and the like. The tackifier is preferably included in the adhesive in amounts of about 10-200 parts by weight, more preferably 50-150 parts by weight, in relation to 100 parts by weigt of the elastic polymer.

The use of the tackifier is especially useful when the copolyester is used as the elastic polymer in the adhesive. When the amount of the tackifier is less than about 10 parts by weight in relation to 100 parts by weight of the elastic polymer, the resultant adhesive tends to have an insufficient adhesive force to fix a wafer for the precise dicing, whereas when the amount of the tackifier is more than about 200 parts by weight, the resultant adhesive is reducible in the adhesive force only to an insufficient extent so that the resultant dice are not readily removable from the dicing film after the dicing by the application of the ultraviolet light, but also the tackifier undesirably tends to migrate onto the dice.

In connection with the tackiness of the dicing film, it is preferable to incorporate both the acrylic acid ester copolymer and the saturated copolyester into an adhesive composition as elastic polymer copmponents, since such an adhesive has a pronouncedly large tackiness, but has substantially no tendency to migrate to dice. This dicing film is especially suitable for industrial use in dicing.

The ultraviolet light polymerizable acrylic acid ester usable in the invention has two or more acryloyl or methacryloyl groups in the molecule and a molecular weight of not more than about 1000. Therefore, the acrylic acid ester usable in the invention includes, for instance, acrylates of polyhydroxy alcohols, such as ethylene glycol diacrylate, 1,6-hexanediol diacrylate, trimethylolpropane triacrylate, tetramethylolmethane tetraacrylate and dipentaerythritol hexaacrylate, and methacrylates of polyhydroxy alcohols, such as ethylene glycol dimethacrylate, 1,6-hexanediol dimethacrylate, trimethylolpropane trimethacrylate, tetramethylolmethane tetramethacrylate and dipentaerythritol pentamethacrylate.

The ultraviolet light photopolymerizable acrylic acid ester is included in the pressure sensitive adhesive in amounts of about 15-200 parts by weight in relation to 100 parts by weight of the elastic polymer. When the photopolymerizable acrylic acid ester is included in amounts less than about 15 parts by weight in relation to 100 parts by weight of the elastic polymer, the resultant adhesive is not substantially reducible in the adhesive force by the application of the ultraviolet light thereto, thereby failing to provide a dicing film to permit the readily removal of dice after dicing of a wafer. Meanwhile when the photopolymerizable acrylic acid ester is included in amounts more than about 200 parts by weight, the adhesive undesirably tends to remain on the dice after the dicing of a wafer, although the resultant adhesive is substantially reducible in the adhesive force by the application of the ultraviolet light.

The pressure sensitive adhesive used in the invention further includes a photopolymerization initiator or photosensitizer, and in addition, may include, when desired, a polymerization inhibitor. The initiator is included in the adhesive to accerelate the polymerization of the photopolymerizable acrylic acid ester as stated hereinvefore, as is well known in the field of the photopolymerization. Any known initiator is usable in the invention, for instance, benzoin alkylethers such as benzoin methylether and benzoin isopropylether, aromatic ketones and aromatic hydroxy ketones such as benzoin, benzil and benzophenone.

The polymerization inhibitor is included in the adhesive, when desired, to prevent the polymerization of the photopolymerizable acrylic acid ester induced by an energy source other than the ultraviolet light, for instance, thermal polymerization. Also the inhibitor usable in the invention is not specifically limited, and as an exemplification, picric acid, phenol, hydroquinone, hydroquinone monomethylether and the like are usable.

The amount of the initiator and the inhibitor used may be in accordance with the amount in the conventional photopolymerization technology, respecitively, and hence the initiator is incorporated in the adhesive in amounts of about 0.1-30 parts by weight, and the inhibitor in amounts of about 0.1-1 parts by weight, respectively, in relation to 100 parts by weight of the photopolymerizable acrylic acid ester, although not limited to these exemplified ranges.

The pressure sensitive adhesive used in the invention may further contain therein a plasticizer such as a polybutene polymer and a mineral oil.

The dicing film used in the invention is composed of a base film and a layer of the pressure sensitive adhesive as set forth above in solid. In the production of the dicing film, the pressure sensitive adhesive is applied preferably in a form of a liquid composition including an organic solvent on to one side of a base film, followed by drying the liquid composition to form a solid layer of the pressure sensitive adhesive on the base film.

The liquid composition as above may be prepared, in principle, by dissolving in an organic solvent such as an aromatic hydrocarbon, an aliphatic ketone or a mixture of these, the above mentioned elastic polymer, photopolymerizable acrylic acid ester, a photopolymerization initiator, and when needed, further additives such as a tackifier, an inhibitor, a filler, an antioxidant and a colorant, each in amounts as stated hereinbefore, respectively. As the organic solvent is preferred in particular a mixture of toluene and methyl ethyl ketone, although not limited thereto. The liquid composition contains the elastic polymer preferably in amounts of about 10-50% by weight based on the liquid adhesive so as to be easy in coating on a base film and drying to form a solid layer of the adhesive on the base film.

The liquid composition may be prepared in any conventional manner known in the field of adhesives. The elastic polymer and the tackifier are usually available in the form of solution in organic solvents. Therefore, it is convenient to prepare the liquid composition, for example, by admixing the solutions of the elastic polymer and the tackifier together, adding to the solution the photopolymerizable acrylic acid ester and the initiator, and when necessary, other additives such as an inhibitor, an antioxidant, a filler or an additional amount of an organic solvent.

As apparent, a liquid composition on the market which includes polyacrylic acid esters as the elastic polymer is also usable for preparing a pressure sensitive adhesive used in the invention, since such a liquid resin composition is in many cases a mixture of the elastic polymer with other additives such as a tackifier and a plasticizer dissolved in an organic solvent, although some of the liquid acrylic acid ester polymer composition are found not to contain a tackifier and a plasticizer.

When the liquid resin composition on the market is used for forming on a base film a solid layer of the preparation of the photopolymerizable pressure sensitive adhesive, the liquid composition is mixed with the photopolymerizable acrylic acid ester and the initiator, and when desired, together with other additional components such as a polymerization inhibitor and an organic solvent, in amounts as stated hereinbefore, depending upon the amount of the elastic polymer in the composition. However, it is preferred that the photopolymerizable acrylic acid ester is admixed in amounts of about 3-60 parts by weight, preferably about 5-20 parts by weight, with 100 parts by weight of the liquid resin composition.

The dicing film used in the invention may be prepared by forming a layer of the pressure sensitive adhesive as set forth hereinbefore on a base film permeable to the ultraviolet light, which will now be described.

Any resin film may be usable as the base film provided that the film is permeable or transparent to the ultraviolet light as well as the film has a strength sufficient to support a semiconductor wafer fixed thereon. The base film usable in the invention, therefore, includes films of polyvinyl chloride, vinyl chloride-vinylidene chloride copolymer, vinyl chloride-vinyl acetate copolymer, vinyl chloride-acrylic acid copolymer, polyvinylidene chloride, polyolefin such as polyethylene or polypropylene, polymethyl methacrylate, polyvinyl alcohol, polyamide, polyimide, polyamideimide, polyester such as polyethylene terephthalate, polycarbonate and cellulose acetate.

Among the above base films, however, films of homopolymers and copolymers of vinyl chloride and vinylidene chloride, respectively, are specifically preferred in the method of the invention, since these films are soft and less expensive than the others. These films, in particular, a polyvinyl chloride film, however, contain therein a plasticizer, although greatly advantageous in price over the other films.

A variety of plasticizers are known, among which are, for instance, diphthalates such as dibutyl phthalate, dioctyl phthalate, didecyl phthalate, di(tricresyl) phthalate and butyl benzyl phthalate; phosphates such as tricresyl phosphate, trioctyl phosphate, triphenyl phosphate, 2-ethylhexyl diphenyl phosphate and cresyl diphenyl phosphate; aliphatic dicarboxylic acid diesters such as dioctyl adipate, dioctyl sebacate, dioctyl azelate and tris(2-ethylhexyl) acetyl citrate; polyester plasticizers such as polypropylene adipate and polypropylene sebacate; epoxidized plasticizers such as epoxidized soybean oils; and chlorinated plasticizers such as chlorinated paraffins and chlorinated fatty acid esters.

It has been found by the inventors that when a layer of the pressure sensitive adhesive is formed directly on a base film which contains the plasticizer therein, the plasticizer migrates into the adhesive, but also the photopolymerizable acrylic acid ester migrates into the base film since the plasticizer has usually a good miscibility with or solubility with respect to the low molecular weight photopolymerizable acrylic acid ester used in the invention.

This bidirectional migration of the plasticizer and the photopolymerizable acrylic acid ester in the dicing film has been found to remarkably decrease the degree of the reduction in the adhesive force of the pressure sensitive adhesive by the application thereto of the ultraviolet light, but also the adhesive force of the adhesive itself has been found to gradually decrease with time.

Therefore, when a resin film which contains a plasticizer is used as the base film of the dicing film, it is desired in the invention that a barrier layer to the bidirectional migration is interposed between the base film and the layer of the pressure sensitive adhesive. The barrier layer is composed of a resin, either in the form of a film or a coating, which is impermeable both to the plasticizer and the photopolymerizable acrylic acid ester but permeable to the ultraviolet light, so that the barrier layer prevents the migration of the plasticizer in the base film into the layer of the adhesive but also the migration of the photopolymerizable acrylic acid ester in the adhesive into the base film. Thus, the barrier layer retains the photopolymerizable acrylic acid ester in the layer of the adhesive as well as retains the plasticizer in the base film, thereby in particular, to retain the function of the dicing film reducible in the adhesive force by the application thereto of the ultraviolet light after a long standing as well as to prevent the reduction in the adhesive force of the adhesive with time before the application thereto of the ultraviolet light.

As the barrier layer mentioned above, a film or a coating of a resin such as polyolefin, e.g., polyethylene or polypropylene, polyalkylene terephthalate, e.g., polyethylene terephthalate, or polymethyl methacrylate, is preferred. The barrier layer is formed, for example, by laminating a film of the resin as specified above on the base film, or by coating a melt or a solution of the barrier resin on the film. Many of the alkyd modified acrylic resin and thermosetting acrylic resins including an acid, a hydroxyl, an epoxy or an amide type thermosetting acrylic resin are also suitable for the barrier coating. However, depending upon the photopolymerizable acrylic acid ester and the plasticizer used, some of the acrylic resins are often found to be soluble therein or swellable therewith, and therefore, when an acrylic resin is used as a barrier resin, it is necessary to choose such an acrylic resin which is neither soluble in nor swellable with the photopolymerizable acrylic acid ester and the plasticizer used.

However, it will be understood that the barrier layer is not limited to the exemplified above, since any layer of a resin may function as the barrier layer if it is impermeable both to the plasticizer and the photopolymerizable acrylic acid ester, but permeable to the ultraviolet light.

Further according to the method of the invention, the pressure sensitive adhesive preferably includes either an anhydrous silica powder or a polyisocyanate or a mixture of these, which causes the reduction to a greater extent in the adhesive force of the adhesive by the application thereto of the ultraviolet light than the adhesive which contained neither the silica nor the polyisocyanate, but otherwise is the same as above.

The silica powder is incorporated into the adhesive in amounts of about 1-30 parts by weight in relation to 100 parts by weight of the elastic polymer. The use of the silica powder in amounts of less than about 1 part by weight in relation to 100 parts by weight of the elastic polymer is insufficient to cause a further extended reduction in the adhesive force by the application thereto of the ultraviolet light, compared with the same adhesive except that it contains no silica powder. However, the use of the silica powder in amounts of more than about 30 parts by weight makes the resultant liquid adhesive composition for forming a solid layer of the pressure sensitive adhesive layer, excessively viscous to form a gel-like substance, and as a result, for instance, the application of the liquid composition onto the base film is difficult. The preferred amount of the silica is about 3-15 parts by weight in relation to 100 parts by weight of the elastic polymer. The silica powder used in the invention is preferably a finely divided powder, and for example, "Aerosil" by Degussa, West Germany, is suitable for use.

A polyisocyanate is also usable for causing a further extended reduction in the adhesive force of the pressure sensitive adhesive by the application thereto of the ultraviolet light when the polyisocyanate is included in the adhesive in amounts of about 1-100 parts by weight in relation to 100 parts by weight of the elastic polymer in the adhesive. When the amount of the polyisocyanate used is less than about 1 part by weight in relation to 100 parts by weight of the elastic polymer, the resultant adhesive is not substantially reduced to an increased extent, whereas when the amount of the polyisocyanate is more than about 100 parts by weight, the resultant adhesive is gradually reduced in the adhesive force with time without the application thereto of the ultraviolet light. The preferred amount of the polyisocyanate is about 3-40 parts by weight in relation to 100 parts by weight of the elastic polymer in the adhesive.

The polyisocyanate usable in the invention is not specifically limited, but a diisocyanate and a triisocyanate are preferably used. The diisocyanate usable includes, for instance, 2,4-toluene diisocyanate, m-phenylene diisocyanate, m-xylylene diisocyanate, 4,4'-diphenyl diisocyanate, 4,4'-diphenylmethane diisocyanate, 1,5-naphthalene diisocyanate, isophorone diisocyanate, dianisidine diisocyanate and hexamethylene diisocyanate, and the triisocyanate usable includes, for instance, trimethylolpropane-toluene diisocyanate adduct.

A urethane prepolymer prepared by the reaction of a diisocyanate in an excess amount with a dihydroxy alcohol so as to have isocyanate groups at the terminals of the polymer is also usable as a polyisocyanate in the invention.

The combined incorporation of the silica and the polyisocyanate results in a synergetic reduction in the adhesive force of the adhesive by the application thereto of the ultraviolet light. As stated hereinbefore, the combined use of the silica and the polyisocyanate in amounts of about 1-30 parts by weight and about 1-100 parts by weight, respectively, in relation to 100 parts by weight of the elastic polymer in the adhesive is allowed in the invention. However, smaller amounts of both of the two are sufficient to bring about the substantial reduction in the adhesive force to an increased extent due to the synergy of the combined use of the two additives. When the two are used in combination, the silica and the polyisocyanate are incorporated usually in amounts of about 1-20 parts by weight, preferably about 1-15 parts by weight, and 1-50 parts by weight, preferably about 1-20 parts by weight, respectively, in relation to 100 parts by weight of the elastic polymer in the adhesive.

According to the method of the invention, a semiconductor wafer is first placed and fixed on the pressure sensitive adhesive on one side of the dicing film. The dicing film has initially an adhesive force, e.g., several hundred grams/25 mm, sufficient to fix the wafer thereon so that the wafer may be diced to discs of a precise size predetermined. Then when the dicing film is irradiated by the ultraviolet light from the other side thereof after the dicing of the wafer, the substantial reduction in the adhesive force of the dicing film takes place, that is, the adhesive force is reduced to several grams/25 mm to several tens grams/25 mm, and as a result, the dice on the dicing film are readily picked up therefrom.

A means and a method for applying the ultraviolet light to the dicing film after the dicing is not specifically limited, but any means and method are applicable to the method of the invention. As an exemplification only, a xenon lamp, a low pressure, a medium pressure or a high pressure mercury lamp is used as a source of the ultraviolet light, and the ultraviolet light is applied to the dicing film after the dicing for a few seconds to a few minutes from the exposed back side of the dicing film to bring about the substantial reduction in the adhesive force of the dicing film.

Further according to the invention, a dicing film may be also usable which has a pressure sensitive adhesive on one side thereof including no photopolymerization initiator. As will be apparent, when this dicing film is used in dicing, an electromagnetic wave which causes polymerization of the before-said photopolymerizable acrylic acid ester other than the ultraviolet light is applied to the back side of the dicing film after dicing. For example, the electron beam is preferred as the electromagnetic wave. In this process, the dicing film is irradiated by the electron beam from the back of the film after the dicing of a semiconductor wafer so that the pressure sensitive adhesive is substantially reduced in the adhesive force. Then the dice are readily removed from the dicing film.

The invention will be more fully understood with reference to the following examples; however these examples are intended to illustrate the invention only, and are not to be construed as limits to the scope of the invention.

EXAMPLE 1

A liquid acrylic resin composition on the market which mainly includes polyacrylic acid esters as the elastic polymer and a tackifier was mixed with a photopolymerizable acrylic acid ester and a photopolymerization initiator, to provide a a liquid composition having the formation as shown in Table 1.

The liquid composition was coated on a mold-releasing paper and dried at 120° C. for 1 minute to form a layer of pressure sensitive adhesive in solid of 10 μm in thickness. A base film of 0.1 mm in thickness and composed of 100 parts by weight of polyvinyl chloride of an average polymerization degree of about 1300, 35 parts by weight of dioctylphthalate and a small amount of an stabilizer was placed on and adhered to the layer of the adhesive, and then the mold-releasing paper was removed, to provide a dicing film which had on one side thereof a pressure sensitive adhesive including the photopolymerizable acrylic acid ester and the photopolymerization initiator according to the invention.

The adhesive force of the dicing film was measured in the manner as follows. The dicing film was cut to a test piece of 25 mm in width and 100 mm in length, and the test piece was placed on a stainless steel plate. The test piece was then pressed against the stainless steel plate by having a 3 kg roll go and return on the dicing film five times, and the 180° adhesive force was measured at a pulling rate of 300 mm/min. with a Schopper's tester.

The adhesive force of the dicing film before the application thereto of the ultraviolet light is presented in Table 1.

                                      TABLE 1                                      __________________________________________________________________________                  References                                                                            Examples                          References                            1  2   1  2   3  4   5  6   7  8   9  10 3  4  5                  __________________________________________________________________________     Formation of Adhesive.sup.1                                                    Polythick 1001S.sup.2                                                                       100    100                                                                               100 100                                                                               100 100                                                                               100    100 100                                                                               100                                                                               100                      Polythick 401SA.sup.3                                                                          100                      100                                   TRP-1.sup.4                                              100                                                                               100                TMPTA.sup.5          3  6   9  9   12     12     20                                                                                40                                                                                70                                                                                12                   DPEHA.sup.6                           9      12              10                Benzoin              1     0.5                                                                                1   1  1   1  1            1  1                 Benzoin isopropylether 0.5                       1  2  2                       Adsesive Force (g/25 mm)                                                       Before UV Irradiation                                                                       750                                                                               950 500                                                                               480 450                                                                               450 500                                                                               400 550                                                                               350 380                                                                               250                                                                               --.sup.7                                                                          100                                                                                50                After UV Irradiation                                                                        700                                                                               900 300                                                                               205  60                                                                                20  1  2   6  0   5  2  0 120                                                                                60                __________________________________________________________________________      Notes:                                                                         .sup.1 Parts by weight                                                         .sup.2 Liquid acrylic adhesive (Sanyo Kasei Kogyo K.K.)                        .sup.3 Liquid acrylic adhesive (Sanyo Kasei Kogyo K.K.)                        .sup.4 Liquid rubber adhesive (Saiden Kagaku K.K.)                             .sup.5 Trimethylolpropane triacrylate                                          .sup.6 Dipentaerythritol hexaacrylate                                          .sup.7 The adhesive was found to migrate onto the stainless steel plate. 

Then the ultraviolet light (365 mμ, 120 W/cm) is applied to the dicing film from the other side thereof for 7 seconds, and the adhesive force was measured, which is presented in Table 1.

The dicing film according to the invention was found to be substantially reduced in the adhesive force by the application thereto of the ultraviolet light.

As a reference, a dicing film was prepared which contained no photopolymerizable acrylic acid ester, but was otherwise the same as above. The dicing film was found to be reduced only slightly in the adhesive force by the application thereto of the ultraviolet light, as presented in Reference Examples 1 and 2 in Table 1.

For a further reference, a dicing film was prepared in the same manner as above except the use of a liquid pressure sensitive adhesive compotion on the market including rubbers as the elastic polymer in place of polyacrylic acid ester coplymers. This dicing film, including the photopolymerizable acrylic acid ester and the initiator, was found to increase in the adhesive force by the application thereto of the ultraviolet light, as presented in Reference Examples 4 and 5.

The dicing film of Reference Example 3 contained the photopolymerizable acrylic acid ester in an excess amount, so that the adhesive was found to remain on the stainless steel plate after the irradiation of the ultraviolet light.

EXAMPLE 2

A mixture of a saturated copolyester, a tackifier, a photopolymerizable acrylic acid ester and an initiator was prepared in a mixed solvent composed of 80% by weight of toluene and 20% by weight of methyl ethyl ketone (the same in the following when a solvent is used), each in amounts specified in Table 2, to provide a liquid composition for forming a pressure sensitive adhesive.

The saturated copolyester used was a condensation product of a saturated dibasic carboxylic acid component consisting of terephthalic acid and sebacic acid in a molar ratio of the former to the latter of 70/30 and ethylene glycol component, in an equimolar ratio, and had a glass transition temperature of about 10° C.

The liquid composition was coated on a mold-releasing paper, and was then dried at 120° C. for one minute to form a layer of a pressure sensitive adhesive in solid of 10 μm in thickness. The same polyvinyl chloride film as used in Example 1 was placed on the layer of the adhesive on the base film, and then the mold-releasing paper was separated therefrom to provide a dicing film according to the invention.

As the adhesive force of the dicing film before and after the appication thereto of the ultraviolet light is presented in Table 2, the substantial reduction in the adhesive force took place by the application of the ultraviolet light.

                                      TABLE 2                                      __________________________________________________________________________                  Examples                                 References                            1  2  3  4  5   6  7  8   9  10 11 12 13 1  2  3                  __________________________________________________________________________     Formation of Adhesive.sup.1                                                    Saturated copolyester                                                                       30 30 30 30 30  30 30 30  30 30 30 30 30 30 30 30                 Xylene resin 30 40 40 40 60  20 25 20  10  5  5  5  5 20 40  5                 Other tackifiers.sup.2                 10 15 15 15 15       15                 Solvent      70 70 70 70 70  70 70 70  70 70 70 70 70 70 70 70                 TMPTA.sup.3        10                                                          DPEHA.sup.4              20     25 30     30 20    20                          TMPTMA.sup.5 10 10    20     12        30       20                             Benzoin             2         2                                                Benzoin isopropylether                                                                       2  2     2  4      4  6   6  6  4  4  4                          Adsesive Force (g/25 mm)                                                       Before UV Irradiation                                                                       525                                                                               450                                                                               610                                                                               600                                                                               750 670                                                                               630                                                                               515 550                                                                               650                                                                               350                                                                               300                                                                               290                                                                               450                                                                               750                                                                               800                After UV Irradiation                                                                        90 100                                                                               85 100                                                                               94  86 60 35  45 50 95 80 88 400                                                                               700                                                                               700                __________________________________________________________________________      Notes:                                                                         .sup.1 Parts by weight                                                         .sup.2 Synthetic hydrocarbon oil in Example 9, terpenephenol resin in          Example 10, aliphatic petroleum resin in Example 11, styrene resin in          Example 12, aliphatic petroleum resin in Example 13, and terpenephenol         resin in Reference 3.                                                          .sup.3 Trimethylolpropane triacrylate                                          .sup.4 Dipentaerythritol hexaacrylate                                          .sup.5 Trimethylolpropane trimethacrylate                                

As a reference, a dicing film was prepared in the same manner as above which contained no photopolymerizable acrylic acid ester, but was otherwise the same as above. The dicing film was found to be reduced only slightly in the adhesive force by the application thereto of the ultraviolet light, as illustrated in Reference Examples 1 to 3 in Table 2.

EXAMPLE 3

By the use of the same saturated copolyester as used in Example 2, a liquid copolyester composition was prepared which had the formation shown in Table 3. The liquid composition was coated on a mold-releasing paper, and then dried at 120° C. for one minute to form a layer of a pressure sesitive adhesive in solid of 10 μm in thickness.

A synthetic resin film of 0.1 mm in thickness as a base film other than polyvinyl chloride film was placed on the layer of the adhesive, and then the mold-releasing paper was separated therefrom to provide a dicing film according to the invention.

As the adhesive force of the dicing film before and after the appication thereto of the ultraviolet light is presented in Table 3, the substantial reduction in the adhesive force was found to take place by the appication of the ultraviolet light.

EXAMPLE 4

A mixture of the same saturated copolyester as used in Example 2, a tackifier, a photopolymerizable acrylic acid ester, an initiator and the same solvent as used in Example 2, each in amounts specified in Table 4, was prepared to provide a liquid copolyester composition for forming on the base film a layer of the pressure sensitive adhesive. The formation of the liquid composition used is presented in Table 4. The liquid composition was coated on a mold-releasing paper, and was then dried at 120° C. for one minute to form a layer of a pressure sensitive adhesive in solid of 10 μm in thickness.

A polyvinyl chloride film of 0.1 mm in thickness was prepared by a calendering process by the use of a composition composed of 100 parts by weight of polyvinyl chloride of an average polymerization degree of about 1300, 35 parts by weight of a plasticizer, either dioctyl phthalate or a polyester plasticizer, and a small amount of a stabilizer.

A barrier layer was then formed which was composed of a resin as shown in Table 4 on the polyvinyl chloride film. The polyvinyl chloride film was placed on the layer of the adhesive so that the barrier layer was in contact with the adhesive, to provide a dicing film having the barrier layer interposed between the base film and the layer of the adhesive according to the invention.

After standing at a predetermined temperature for a predetermined period of time, the mold-releasing paper was removed, and the adhesive force of the film was measured. Then the film was irradiated by the ultraviolet light from the back side thereof in the same manner as in Example 1, and the adhesive force was measured. The change in the adhesive force before and after the irradiation of the ultraviolet light is presented in Table 4.

                  TABLE 3                                                          ______________________________________                                                      Examples                                                                       1      2      3        4                                          ______________________________________                                         Formation of Adhesive.sup.1                                                    Saturated copolyester                                                                         30       30     30     30                                       Xylene resin   30       20     30     20                                       Solvent        70       70     70     70                                       TMPTA.sup.2             30                                                     DPEHA.sup.3    30              30     30                                       Benzoin isopropylether                                                                         4        4      6      6                                       Base Film.sup.4                                                                               PET      PP     PA     PMMA                                     Adsesive Force (g/25 mm)                                                       Before UV Irradiation                                                                         450      400    300    250                                      After UV Irradiation                                                                          45       40     33     48                                       ______________________________________                                          Notes:                                                                         .sup.1 Parts by weight                                                         .sup.2 Trimethylolpropane triacrylate                                          .sup.3 Dipentaerythritol hexaacrylate                                          .sup.4 PET: Polyethylene terephthalate                                         PP: Polypropylene                                                              PA: Polyamide                                                                  PMMA: Polymethyl methacrylate                                            

                  TABLE 4                                                          ______________________________________                                                    Examples      References                                                       1    2      3      4    1     2                                     ______________________________________                                          Formation of                                                                  Adhesive.sup.1                                                                 Saturated copolyester                                                                        30    30     30   30   30    30                                  Xylene resin  20    20     15   15   20    20                                  Solvent       70    70     70   70   70    70                                  TMPTA.sup.2                30   30                                             DPEHA.sup.3   30    20               30                                        Benzoin isopropyl-                                                                           6      6      6    6    6                                        ether                                                                          Barrier Layer.sup.4                                                                         Ac     Ac     PP   PE   None  None                                Adsesive Force                                                                 (g/25 mm)                                                                      Initial                                                                        Before UV Irradiation                                                                       510    470    350  300  560   450                                 After UV Irradiation                                                                         62    40     56   45   35    400                                 After standing at                                                              80° C. for 1 day                                                        Before UV Irradiation                                                                       530    435    300  280  20                                        After UV Irradiation                                                                         50    42     50   55   100                                       After standing at                                                              80° C. for 3 days                                                       Before UV Irradiation                                                                       450    450    310  285   0                                        After UV Irradiation                                                                         52    45     40   38   25                                        After standing at                                                              80°  C. for 5 days                                                      Before UV Irradiation                                                                       480    425    290  275                                            After UV Irradiation                                                                         38    50     45   40                                             After standing at                                                              normal temperature                                                             for 1 month                                                                    Before UV Irradiation                                                                       500    400    300  280  325                                       After UV Irradiation                                                                         55    45     48   56   25                                        After standing at                                                              normal temperature                                                             for 3 months                                                                   Before UV Irradiation                                                                       450    420    310  250   0                                        After UV Irradiation                                                                         45    50     42   32   15                                        ______________________________________                                          Notes:                                                                         .sup.1 Parts by weight                                                         .sup.2 Trimethylolpropane triacrylate                                          .sup.3 Dipentaerythritol hexaacrylate                                          .sup.4 Ac: Coating of modified acrylic resin                                   PP: Polypropylene film                                                         PE: Polyethylene film                                                    

The dicing film according to the invention was found to be substantially reduced in the adhesive force by the application thereto of the ultraviolet light even after a long standing.

As a reference, a dicing film was prepared which contained no barrier layer, but was otherwise the same as above. As presented in Reference Example 1 in Table 4, the dicing film of reference, immediately after the preparation, was found to be substantially reduced in the adhesive force by the application thereto of the ultraviolet light, but after a long standing the dicing film was found to have a tendency of being reduced irregularly in the adhesive force with time without the application thereto of the ultraviolet light.

Further, the dicing film of reference was often found to increase in the adhesive force by the application thereto of the ultraviolet light after a long standing, contrary to the dicing film according to the invention.

As a further reference, a dicing film was prepared which contained no photopolymerizable acrylic acid ester, but was otherwise the same as above. This dicing film was found to be substantially unchanged in the adhesive force by the application thereto of the ultraviolet light even immediately after the preparation.

EXAMPLE 5

A liquid acrylic resin composition on the market (Polythick 610SA, Sanyo Kasei Kogyo K.K.) including polyacrylic acid ester coplymers in amounts of about 40% by weight based on the composition as the elastic polymer was mixed with a photopolymerizable acrylic acid ester and an initiator, each in amounts specified in Table 5, and then the resulting liquid composition was coated on a mold-releasing paper, and was then dried at 120° C. for one minute to form a layer of a pressure sensitive adhesive in solid of 10 μm in thickness.

In the same manner as in Example 4, a barrier layer was formed on the same polyvinyl chloride film as used in Example 4, and a dicing film having the barrier layer between the base film and the layer of the adhesive was prepared.

The dicing film according to the invention was found to be substantially reduced in the adhesive force by the application thereto of the ultraviolet light even after a long standing, as illustrated in Table 5.

As a reference, a dicing film was prepared which contained no photopolymerizable acrylic acid ester, but was otherwise the same as above. The dicing film was found to be substantially unchanged in the adhesive force by the application thereto of the ultraviolet light even immediately after the preparation, as illustrated in Reference Example 1 in Table 5.

                  TABLE 5                                                          ______________________________________                                                           Examples   Refer-                                                              1    2      3      ence 1                                    ______________________________________                                         Formation of Adhesive.sup.1                                                    Liquid acrylic adhesive                                                                            100    100    100  100                                     TMPTA.sup.2          30     20                                                 DPEHA.sup.3                        30                                          Benzoin isopropylether                                                                              6      6      6                                           Barrier Layer.sup.4 Ac     Ac     Ac   Ac                                      Adsesive Force (g/25 mm)                                                       Initial                                                                        Before UV Irradiation                                                                              690    700    720  710                                     After UV Irradiation                                                                                58     68     50  690                                     After standing at 80° C. for 1 day                                      Before UV Irradiation                                                                              650    700    710                                          After UV Irradiation                                                                                54     60     50                                          After standing at 80° C. for 3 days                                     Before UV Irradiation                                                                              700    720    600                                          After UV Irradiation                                                                                56     62     48                                          After standing at 80° C. for 5 days                                     Before UV Irradiation                                                                              650    690    650                                          After UV Irradiation                                                                                60     68     52                                          After standing at normal temperature                                           for 1 month                                                                    Before UV Irradiation                                                                              660    650    620                                          After UV Irradiation                                                                                60     70     65                                          After standing at normal temperature                                           for 3 months                                                                   Before UV Irradiation                                                                              620    680    600                                          After UV Irradiation                                                                                54     58     60                                          ______________________________________                                          Notes:                                                                         .sup.1 Parts by weight                                                         .sup.2 Trimethylolpropane triacrylate                                          .sup.3 Dipentaerythritol hexaacrylate                                          .sup.4 Ac: Coating of modified acrylic resin                             

EXAMPLE 6

A mixture of the same saturated copolyester as used in Example 2, a tackifier, a photopolymerizable acrylic acid ester, an initiator, the same solvent as used in Example 2 and anhydrous silica powder ("Aerosil" (Trademark), Degussa, West Germany, the same in the following), each in amounts specified in Table 6, was prepared to provide a liquid composition which had the formation as shown in Table 6. The composition was coated on a mold-releasing paper, and then was dried at 120° C. for one minute to form a layer of a pressure sensitive adhesive in solid of 10 μm in thickness.

A barrier layer was formed on the same polyvinyl chloride film as used in Example 4 by coating a solution of modified acrylic resin on the market followed by drying, and the polyvinyl chloride film was then placed on the layer of the adhesive so that the barrier layer was in contact with the adhesive, to provide a dicing film having the barrier layer interposed between the base film and the layer of the adhesive according to the invention.

After standing at a predetermined temperature for a predetermined period of time, the mold-releasing paper was removed, and the adhesive force of the dicing film was measured. Then the dicing film was irradiated by the ultraviolet light from the back side thereof in the same manner as in Example 1, followed by the measurement of the adhesive force. The change in the adhesive force is presented in Table 6.

As a reference, a dicing film was prepared which contained no silica powder but was otherwise the same as above.

First the dicing film containing the silica powder was found to be substantially reduced in the adhesive force by the application thereto of the ultraviolet light even after a long standing. Second the dicing film containing the silica powder was found to be reduced in the adhesive force to a greater extent than the dicing film containing no silica powder therein, but otherwise the same, as apparent from the comparison with Reference Examples 1 and 2 in Table 6.

However, it is to be noted that the dicing film of Reference Examples 1 and 2 are still within the scope of the present invention.

EXAMPLE 7

The same liquid acrylic resin composition as used in Example 5 was mixed with a photopolymerizable acrylic acid ester, an initiator and the same anhydrous silica powder used in Example 6, each in amounts specified in Table 7, to provide a liquid composition having the formation as shown in Table 7. The composition was coated on a mold-releasing paper, and then was dried at 120° C. for one minute to form a layer of a pressure sensitive adhesive in solid of 10 μm in thickness.

                                      TABLE 6                                      __________________________________________________________________________                       Examples       References                                                      1  2  3  4  5  1  2                                          __________________________________________________________________________     Formation of Adhesive.sup.1                                                    Saturated copolyester                                                                            30 30 30 30 30 30 30                                         Xylene resin      15 15 15 15 15 15 15                                         Solvent           70 70 70 70 70 70 70                                         TMPTA.sup.2       20 20 20 30    20 30                                         DPEHA.sup.3                   30                                               Benzoin            6  6  6  6                                                  Benzoin isopropylether         6  6  6                                         Silica.sup.4       1  3  5  3  3  0  0                                         Adsesive Force (g/25 mm)                                                       Initial                                                                        Before UV Irradiation                                                                            530                                                                               480                                                                               610                                                                               300                                                                               525                                                                               470                                                                               520                                        After UV Irradiation                                                                             40 25 20 45 42 75 60                                         After standing at 80° C. for 1 day                                      Before UV Irradiation                                                                            525                                                                               480                                                                               570                                                                               280                                                                               500                                                                               490                                                                               515                                        After UV Irradiation                                                                             38 30 18 55 34 80 58                                         After standing at 80°  C. for 3 days                                    Before UV Irradiation                                                                            535                                                                               510                                                                               550                                                                               285                                                                               495                                                                               500                                                                               500                                        After UV Irradiation                                                                             35 30 25 38 30 78 70                                         After standing at 80° C. for 5 days                                     Before UV Irradiation                                                                            540                                                                               450                                                                               545                                                                               275                                                                               500                                                                               485                                                                               524                                        After UV Irradiation                                                                             35 28 20 40 32 68 66                                         After standing at normal temperature                                           for 1 month                                                                    Before UV Irradiation                                                                            540                                                                               500                                                                               580                                                                               280                                                                               520                                                                               500                                                                               510                                        After UV Irradiation                                                                             35 35 30 56 38 70 60                                         After standing at normal temperature                                           for 3 months                                                                   Before UV Irradiation                                                                            500                                                                               470                                                                               550                                                                               250                                                                               525                                                                               492                                                                               498                                        After UV Irradiation                                                                             33 20 25 32 35 68 72                                         __________________________________________________________________________      Notes:                                                                         .sup.1 Parts by weight                                                         .sup.2 Trimethylolpropane triacrylate                                          .sup.3 Dipentaerythritol hexaacrylate                                          .sup.4 "Aerosil," Degussa, West Germany                                  

                  TABLE 7                                                          ______________________________________                                                              Examples                                                                       1    2                                                    ______________________________________                                         Formation of Adhesive.sup.1                                                    Liquid acrylic adhesive                                                                               100    100                                              DPEHA.sup.2            30     30                                               Benzoin isopropylether  6      6                                               Silica.sup.3            5     10                                               Adsesive Force (g/25 mm)                                                       Initial                                                                        Before UV Irradiation  700    800                                              After UV Irradiation   30     28                                               After standing at 80° C. for 1 day                                      Before UV Irradiation  720    780                                              After UV Irradiation   25     25                                               After standing at 80° C. for 3 days                                     Before UV Irradiation  700    750                                              After UV Irradiation   28     25                                               After standing at 80° C. for 5 days                                     Before UV Irradiation  690    700                                              After UV Irradiation   30     20                                               After standing at normal temperature                                           for 1 month                                                                    Before UV Irradiation  685    725                                              After UV Irradiation   30     25                                               After standing at normal temperature                                           for 3 months                                                                   Before UV Irradiation  654    700                                              After UV Irradiation   26     24                                               ______________________________________                                          Notes:                                                                         .sup.1 Parts by weight                                                         .sup.2 Dipentaerythritol hexaacrylate                                          .sup.3 "Aerosil," Degussa, West Germany                                  

A barrier layer was then formed in the same manner as in Example 6 on the same polyvinyl chloride film as used in Example 4, and the polyvinyl chloride film was then placed on the layer of the adhesive, to provide a dicing film having the barrier layer between the base film and the layer of the adhesive according to the invention.

The dicing film containing the silica powder was found to be substantially reduced in the adhesive force by the application thereto of the ultraviolet light even after a long standing.

EXAMPLE 8

In the same manner as in Example 6 except the use of a polyisocyanate in place of the silica powder, a dicing film having the same barrier coating of modified acrylic resin as the beforementioned was prepared. The formation of the liquid coplyester composition used for the pressure sensitive adhesive is shown in Table 8.

As a reference, a dicing film was prepared in the same manner as in Example 6 except that the film contained no polyisocyanate.

The dicing film containing the polyisocyanate was found to be substantially reduced in the adhesive force by the application thereto of the ultraviolet light even after a long standing, but also was found to be reduced in the adhesive force to a greater extent than the dicing film containing no polyisocyanate therein, as illustrated in comparison with Reference Examples 1 and 2 in Table 8.

EXAMPLE 9

The same liquid acrylic resin composition as used in Example 5 was mixed with a photopolymerizable acrylic acid ester, an initiator and a polyisocyanate, each in amounts specified in Table 9, to provide a liquid composition having the formation as shown in Table 9.

By the use of the liquid composition thus prepared, a dicing film was prepared in the same manner as in Example 6 having the same barrier coating of modified acrylic resin as beforementioned between the base film and the pressure sensitive adhesive.

The dicing film containing the polyisocyanate was found to be substantially reduced in the adhesive force by the application thereto of the ultraviolet light even after a long standing, as illustrated in Table 9.

EXAMPLE 10

In the same manner as in Example 6 except the combined use of silica powder and the polyisocyanate, a dicing film having the same barrier coating of modified acrylic resin as beforementioned was prepared. The formation of the liquid composition is shown in Table 10.

                                      TABLE 8                                      __________________________________________________________________________                       Examples       References                                                      1  2  3  4  5  1  2                                          __________________________________________________________________________     Formation of Adhesive.sup.1                                                    Saturated copolyester                                                                            30 30 30 30 30 30 30                                         Xylene resin      20 20 20 20 15 15 25                                         Solvent           70 70 70 70 70 70 70                                         TMPTA.sup.2                   20    20                                         DPEHA.sup.3       30 30 30 30    30                                            Benzoin            6                                                           Benzoin isopropylether                                                                               6  6  6  4  6  4                                         Polyisocyanate.sup.4                                                                              2  5 10 20  5  0  0                                         Adsesive Force (g/25 mm)                                                       Initial                                                                        Before UV Irradiation                                                                            500                                                                               495                                                                               350                                                                               350                                                                               550                                                                               525                                                                               525                                        After UV Irradiation                                                                             35 32 25 18 30 60 85                                         After standing at 80° C. for 1 day                                      Before UV Irradiation                                                                            480                                                                               510                                                                               300                                                                               250                                                                               500                                                                               515                                                                               530                                        After UV Irradiation                                                                             40 30 28 15 45 55 78                                         After standing at 80° C. for 3 days                                     Before UV Irradiation                                                                            520                                                                               500                                                                               325                                                                               200                                                                               480                                                                               500                                                                               550                                        After UV Irradiation                                                                             32 28 25 20 40 60 80                                         After standing at 80° C. for 5 days                                     Before UV Irradiation                                                                            490                                                                               515                                                                               350                                                                               200                                                                               490                                                                               505                                                                               525                                        After UV Irradiation                                                                             20 26 24 12 35 62 75                                         After standing at normal temperature                                           for 1 month                                                                    Before UV Irradiation                                                                            490                                                                               500                                                                               392                                                                               300                                                                               510                                                                               525                                                                               530                                        After UV Irradiation                                                                             40 30 28 20 38 55 80                                         After standing at normal temperature                                           for 3 months                                                                   Before UV Irradiation                                                                            510                                                                               510                                                                               350                                                                               200                                                                               500                                                                               510                                                                               530                                        After UV Irradiation                                                                             38 32 30 16 36 58 70                                         __________________________________________________________________________      Notes:                                                                         .sup.1 Parts by weight                                                         .sup.2 Trimethylolpropane triacrylate                                          .sup.3 Dipentaerythritol hexaacrylate                                          .sup.4 Triisocyanate "Sumidule," Sumitomo Kagaku Kogyo K.K.              

                  TABLE 9                                                          ______________________________________                                                              Examples                                                                       1    2                                                    ______________________________________                                         Formation of Adhesive.sup.1                                                    Liquid acrylic adhesive                                                                               100    100                                              DPEHA.sup.2            30     30                                               Benzoin isopropylether  6      6                                               Polyisocyanate.sup.3    5     10                                               Adsesive Force (g/25 mm)                                                       Initial                                                                        Before UV Irradiation  620    670                                              After UV Irradiation   35     25                                               After standing at 80° C. for 1 day                                      Before UV Irradiation  570    580                                              After UV Irradiation   28     14                                               After standing at 80° C. for 3 days                                     Before UV Irradiation  590    610                                              After UV Irradiation   30     20                                               After standing at 80° C. for 5 days                                     Before UV Irradiation  600    595                                              After UV Irradiation   30     18                                               After standing at normal temperature                                           for 1 month                                                                    Before UV Irradiation  600    650                                              After UV Irradiation   30     20                                               After standing at normal temperature                                           for 3 months                                                                   Before UV Irradiation  570    580                                              After UV Irradiation   28     22                                               ______________________________________                                          Notes:                                                                         .sup.1 Parts by weight                                                         .sup.2 Dipentaerythritol hexaacrylate                                          .sup.3 Triisocyanate "Sumidule," Sumitomo Kagaku Kogyo K.K.              

As a reference, a dicing film was prepared which contained only one of silica powder and the polyisocyanate.

The dicing film containing both the polyisocyanate and the silica was found to be reduced in the adhesive force to a greater extent by the application thereto of the ultraviolet light than the dicing film containing only one of the polyisocyanate and the silica, as illustrated in comparison with Reference Examples 1 and 2 in Table 10.

However, the dicing films of Reference Examples 1 and 2 are still greater in the degree of reduction in the adhesive force by the application thereto of the ultraviolet light than the dicing films of Reference Examples 3 and 4 which contained neither the silica nor the polyisocyanate. It is also to be noted that these dicing films of Reference Examples 1 to 4 are all substantially reducible in the adhesive by the ultraviolet irradiation and are within the scope of the present invention.

EXAMPLE 11

The same acrylic liquid composition for a pressure sensitive adhesive as used in Exaple 5 was mixed with a photopolymerizable acrylic acid ester, an initiator, the polyisocyanate and the silica powder, each in amounts specified in Table 11, to provide a liquid composition for the pressure sensitive adhesive. The formation of the liquid composition is shown in Table 11.

                                      TABLE 10                                     __________________________________________________________________________                       Examples       References                                                      1  2  3  4  5  1  2  3  4                                    __________________________________________________________________________     Formation of Adhesive.sup.1                                                    Saturated copolyester                                                                            30 30 30 30 30 30 30 30 30                                   Xylene resin      15 20 30 30 20 20 15 20 15                                   Solvent           70 70 70 70 70 70 70 70 70                                   TMPTA.sup.2             30    20                                               DPEHA.sup.3       30 30    30    30 30 30 30                                   Benzoin            6           4                                               Benzoin isopropylether                                                                               4  6  6     6  6  6  6                                   Polyisocyanate.sup.4                                                                              2  3  3  2  2  5  0  0  0                                   Silica.sup.(5)     2  5  5  5  2  0  3  0  0                                   Adsesive Force (g/25 mm)                                                       Initial                                                                        Before UV Irradiation                                                                            492                                                                               550                                                                               480                                                                               510                                                                               610                                                                               495                                                                               525                                                                               510                                                                               350                                  After UV Irradiation                                                                               8                                                                                6  5 10 20 32 42 62 56                                   After standing at 80° C. for 1 day                                      Before UV Irradiation                                                                            510                                                                               545                                                                               450                                                                               525                                                                               600                                                                               510                                                                               500                                                                               530                                                                               300                                  After UV Irradiation                                                                             10 14  4  8 18 30 34 50 50                                   After standing at 80° C. for 3 days                                     Before UV Irradiation                                                                            460                                                                               500                                                                               465                                                                               514                                                                               570                                                                               500                                                                               495                                                                               450                                                                               310                                  After UV Irradiation                                                                              4  4 10 12 12 28 30 52 40                                   After standing at 80° C. for 5 days                                     Before UV Irradiation                                                                            500                                                                               525                                                                               485                                                                               520                                                                               550                                                                               515                                                                               500                                                                               485                                                                               290                                  After UV Irradiation                                                                              2  2  8 10 14 26 32 38 45                                   After standing at normal temperature                                           for 1 month                                                                    Before UV Irradiation                                                                            472                                                                               550                                                                               480                                                                               500                                                                               540                                                                               500                                                                               520                                                                               500                                                                               300                                  After UV Irradiation                                                                             10  5  4 13 18 30 38 55 48                                   After standing at normal temperature                                           for 3 months                                                                   Before UV Irradiation                                                                            514                                                                               500                                                                               470                                                                               498                                                                               520                                                                               510                                                                               525                                                                               450                                                                               310                                  After UV Irradiation                                                                             17 14  6 10 13 32 35 45 42                                   __________________________________________________________________________      Notes:                                                                         .sup.1 Parts by weight                                                         .sup.2 Trimethylolpropane triacrylate                                          .sup.3 Dipentaerythritol hexaacryalate                                         .sup.4 Triisocyanate "Sumidule," Sumitomo Kagaku Kogyo K.K.                    .sup.5 "Aerosil," Degussa, West Germany                                  

                                      TABLE 11                                     __________________________________________________________________________                       Examples       References                                                      1  2  3  4  5  1  2  3                                       __________________________________________________________________________     Formation of Adhesive.sup.1                                                    Liquid acrylic adhesive                                                                          100                                                                               100                                                                               100                                                                               100                                                                               100                                                                               100                                                                               100                                                                               100                                     DPEHA.sup.2       20 30 30 30 20 30 30 30                                      Benzoin isopropylether                                                                            6  6  6  6  6  6  6  6                                      Polyisocyanate.sup.3                                                                              1  2  3  5 10  5  0  0                                      Silica.sup.4       2  2  5  3  2  0  3  0                                      Adsesive Force (g/25 mm)                                                       Initial                                                                        Before UV Irradiation                                                                            700                                                                               600                                                                               605                                                                               620                                                                               700                                                                               620                                                                               600                                                                               510                                     After UV Irradiation                                                                             20  8  6  6 12 35 50 70                                      After standing at 80° C. for 1 day                                      Before UV Irradiation                                                                            680                                                                               625                                                                               630                                                                               620                                                                               600                                                                               570                                                                               588                                                                               500                                     After UV Irradiation                                                                             18 10  4  6  2 28 42 68                                      After standing at 80° C. for 3 days                                     Before UV Irradiation                                                                            720                                                                               650                                                                               610                                                                               650                                                                               549                                                                               590                                                                               602                                                                               508                                     After UV Irradiation                                                                             12  4  4  4 12 30 38 75                                      After standing at 80° C. for 5 days                                     Before UV Irradiation                                                                            800                                                                               700                                                                               600                                                                               600                                                                               550                                                                               600                                                                               598                                                                               512                                     After UV Irradiation                                                                             18  4 12 12  4 30 40 78                                      After standing at normal temperature                                           for 1 month                                                                    Before UV Irradiation                                                                            650                                                                               650                                                                               625                                                                               600                                                                               680                                                                               600                                                                               590                                                                               520                                     After UV Irradiation                                                                             22 15  5 12  4 30 42 80                                      After standing at normal temperature                                           for 3 months                                                                   Before UV Irradiation                                                                            600                                                                               595                                                                               580                                                                               570                                                                               600                                                                               570                                                                               600                                                                               500                                     After UV Irradiation                                                                             20  6  4  4  2 28 44 82                                      __________________________________________________________________________      Notes:                                                                         .sup.1 Parts by weight                                                         .sup.2 Dipentaerythritol hexaacrylate                                          .sup.3 Triisocyanate "Sumidule," Sumitomo Kagaku Kogyo K.K.                    .sup.4 "Aerosil," Degussa, West Germany                                  

By the use of the liquid composition thus prepared, a dicing film was prepared in the same manner as in Example 6 having the same barrier coating of modified acrylic resin.

The dicing film containing the polyisocyanate and the silica powder was found to be reduced in the adhesive force to a greater extent than the dicing film containing only one of the polyisocyanate and the silica powder, as illustrated in comparison with Reference Examples 1 and 2 in Table 11.

The dicing film of Examples 1 and 2 are, however, still greater in the degree of reduction in the adhesive force when being irradiated by the ultraviolet light than the dicing film of Reference Example 3, and are in accordance with the invention. The dicing film of Example 3 is also a film usable in the invention.

EXAMPLE 12

The same liquid acrylic acid ester copolymer composition as used in Example 5 and the same saturated copolyester as used in Example 2 were both incorporated into a liquid composition together with a solvent, a tackifier, dipentaerythritol hexaacrylate, benzoin isopropylether, silica and a polyisocyanate. The formation of the resultant liquid composition is presented in Table 12.

By the use of the liquid composition, a dicing film was prepared in the same manner as in Example 6 having the same barrier coating of modified acrylic resin as beforesaid between the polyvinyl chloride base film and the pressure sensitive adhesive.

The tackiness and adhesive migration were measured as follows.

Tackiness:

A dicing film was fixed on a horizontal plane at 21° C. with the layer of adhesive exposed, and a stainless steel plate was supported on the plane so that the plate intersected at the lower end with the plane at an angle of 30°. A stainless steel ball of 8.0 mm in diameter and 2.0 g in weight was placed on the steel plate at a position 50 mm apart from the lower end of the plate, and then was allowed to roll down on the slope. The tackiness was estimated in terms of the distance between the lower end of the steel plate and the position at which the ball stopped.

Adhesive migration:

A dicing film of 25 mm in width and 100 mm in length was adhered onto a stainless steel plate and was left standing at a predetermined period of time at 21° C. Thereafter the film was separated from the plate at a pulling rate of 300 mm/min. by a Schopper's tester, and the plate was examined whether the adhesive was migrated thereonto.

The above dicing film was found to have a pronouncedly large tackiness, but substantially no adhesive was found on the plate even after a long standing of seven days, as shown in Table 12.

As a reference example, a dicing film was prepared which included only the saturated copolyester as an elastic polymer. The formation of the liquid composition used is presented in Table 12.

The reference dicing film was found to have a smaller tackiness, and at the same time the adhesive was found to migrate onto the plate. However, it is to be noted that the dicing films of Reference Examples 1 and 2 are in accordance with the invention and are also usable in the process of the invention.

                                      TABLE 12                                     __________________________________________________________________________                       Examples        References                                                     1   2   3   4   1   2                                        __________________________________________________________________________     Formation of Adhesive.sup.1                                                    Polythick 610SA.sup.2                                                                            20  40  60  80                                               Saturated coplyester                                                                             24  18  12  6   30  30                                       Xylene resin      15  15  15  15  15  15                                       Solvent           56  42  28  14  70  70                                       DPEHA.sup.3       30  30  30  30  30  30                                       Benzoin isopropyl ether                                                                          6   6   6   6   6   6                                        Silica.sup.4      4   4   4   6   2   4                                        Polyisocyanate.sup.5                                                                             7   7   7   9   5   7                                        Adsesive Force (g/25 mm)                                                       Initial                                                                        Before UV Irradiation                                                                            500 610 650 625 620 585                                      After UV Irradiation                                                                             18  17  14  20  12  10                                       After standing at 80° C. for 7 days                                     Before UV Irradiation                                                                            520 550 650 600 600 550                                      After UV Irradiation                                                                             15  13  12  18  13  12                                       After standing at normal temperature                                           for 3 months                                                                   Before UV Irradiation                                                                            550 590 620 630 625 590                                      After UV Irradiation                                                                             12  15  18  20  10  10                                       Tackiness at 21° C. (cm)                                                                  1.2 1.0 0.5 0.7 6.5 5.3                                      Initial (Before UV Irradiation)                                                 Adhesive Migration (21° C.).sup.6                                      After 1 day       1   1   1   1   4   3                                        After 4 days      1   1   1   1   5   5                                        After 7 days      1   1   2   1   5   5                                        __________________________________________________________________________      Notes:                                                                         .sup.1 Parts by weight                                                         .sup.2 Liquid acrylic adhesive (Sanyo Kasei Kogyo K.K.)                        .sup.3 Dipentaerythritol hexaacrylate                                          .sup.4 "Aerosil," Degussa, West Germany                                        .sup.5 Triisocyanate "Sumidule," Sumitomo Kagaku Kogyo K.K.                    .sup.6 Five grade estimation; the more the figure, the more the migration                                                                                

What is claimed is:
 1. A method for dicing a semiconductor wafer to form dice which comprises:(a) placing and fixing the wafer on a dicing film which comprises a base film permeable to ultraviolet light and a layer of a pressure sensitive adhesive formed on one side of the base film to fix thereon the wafer, the adhesive comprising:(i) at least one elastic polymer selected from the group consisting of a polymer comprising acrylic acid ester copolymers, and a saturated copolyester comprising a dibasic carboxylic acid and a dihydroxy alcohol; (ii) and ultraviolet light polymerizable acrylic acid ester having not less than two acryloyl or methacryloyl groups in the molecule and having a molecular weight of not more than about 1000, in amounts of about 15-200 parts by weight in relation to 100 parts by weight of the elastic polymer; (iii) a tacifier in amounts of about 10-200 parts by weight in relation to 100 parts by weight of the elastic polymer; (iv) anhydrous silica powder in amounts of about 1-30 parts by weight in relation to 100 parts by weight of the elastic polymer; and (v) a photopolymerization initiator in a sufficient amount to induce the photopolymerization of the ultraviolet light polymerizable acrylic acid ester; (b) dicing the wafer; (c) applying the ultraviolet light to the other side of the dicing film to substantially reduce the adhesive force of the dicing film; and (d) removing the resultant dice from the dicing film.
 2. The method as claimed in claim 1 wherein the pressure sensitive adhesive includes a polyisocyanate in amounts of about 1-100 parts by weight in relation to 100 parts by weight of the elastic polymer.
 3. The method as claimed in claim 1 wherein the base film contains a plasticizer and has a barrier layer composed of a resin permeable to the ultraviolet light but impermeable to both the ultraviolet light polymerizable acrylic acid ester and the plasticizer between the base film and the layer of the adhesive.
 4. The method as claimed in claim 3 wherein the base film is a polyvinyl chloride film.
 5. The method as claimed in claim 3 wherein the barrier layer is composed of a resin selected from the group consisting of polyethylene, polypropylene, polymethyl methacrylate and polyethylene terephthalate.
 6. The method as claimed in claim 3 wherein the barrier layer is composed of a coating of a modified acrylic resin selected from the group consisting of alkyd modified acrylic resin and a thermosetting acrylic resin.
 7. A method for dicing a semiconductor wafer to form dice which comprises:(a) placing and fixing the wafer on a dicing film which comprises a base film permeable to an electromagnetic wave and a layer of a pressure sensitive adhesive formed on one side of the base film to fix thereon the wafer, the adhesive comprising:(i) at least one elastic polymer selected from the group consisting of a polymer comprising acrylic acid ester copolymers, and a saturated copolyester comprising a dibasic carboxylic acid and a dihydroxy alcohol; (ii) an ultraviolet light polymerizable acrylic acid ester having not less than two acryloyl or methacryloyl groups in the molecule and having a molecular weight of not more than about 1000, in amounts of about 15-200 parts by weight in relation to 100 parts by weight of the elastic polymer; (iii) a tackifier in amounts of about 10-200 parts by weight in relation to 100 parts by weight of the elastic polymer; and (iv) anhydrous silica powder in amounts of about 1-30 parts by weight in relation to 100 parts by weight of the elastic polymer; (b) dicing the wafer; (c) applying electromagnetic waves to the other side of the dicing film to substantially reduce the adhesive force of the dicing film; and (d) removing the resultant dice from the dicing film.
 8. The method as claimed in claim 7 wherein the electomagnetic wave is an electron beam.
 9. The method as claimed in claim 7 wherein the pressure sensitive adhesive further includes a polyisocyanate in amounts of about 1-100 parts by weight in relation to 100 parts by weight of the elastic polymer.
 10. The method as claimed in claim 7 wherein the base film contains a plasticizer and has a barrier layer composed of a resin permeable to the electromagnetic wave but impermeable to both the electromagnetic wave polymerizable acrylic acid ester and the plasticizer between the base film and the layer of the adhesive.
 11. The method as claimed in claim 10 wherein the base film is a polyvinyl chloride film.
 12. The method as claimed in claim 10 wherein the barrier layer is composed of a resin selected from the group consisting of polyethylene, polypropylene, polymethyl methacrylate and polyethylene terephthalate.
 13. The method as claimed in claim 12 wherein the barrier layer is composed of a coating of a modified acrylic resin selected from the group consisting of alkyd modified acrylic resin and a thermosetting acrylic resin. 